Fast Curing Carbon Fiber Fabric Prepregs Description:
Fast Curing Carbon Fiber Fabric Prepregs are high-performance composite materials consisting of carbon fiber fabrics pre-impregnated with a resin system engineered for rapid curing, often in just 3 to 10 minutes. These prepregs offer excellent strength, stiffness, and lightweight properties, making them ideal for structural applications. With good workability and compatibility with processes like compression molding and autoclaving, they are widely used in industries such as automotive, aerospace, sports equipment, and wind energy, where fast production cycles and high-performance materials are essential.
Fast Curing Carbon Fiber Fabric Prepregs Specifications:
|
Exterior Appearance
|
Black Plain
|
|
Material
|
Carbon Fiber - Thermosetting fast curing epoxy resin
|
|
Gel Time of Resin
|
11min-14min@110℃
|
|
Curing Temperature of Resin
|
110℃-130℃
|
|
Length
|
100m/roll
|
|
Fiber Areal Weight
|
200 g/m2
|
|
Resin Content
|
42
|
|
Total Areal Weight
|
345 g/m2
|
|
Thickness
|
0.23 mm
|
Regular Specifications
|
Brand
|
Model
|
FAW (g/m2)
|
RC（%）
|
TAW (g/m2)
|
Thickness (mm)
|
|
UTFC-200CP
|
Plain
|
200
|
42
|
345
|
0.23
|
|
UTFC-200CT
|
Twill
|
200
|
42
|
345
|
0.23
|
Fast Curing Carbon Fiber Fabric Prepregs Applications:
1. Automotive Industry: Used in manufacturing lightweight, high-strength components such as body panels, chassis parts, and structural reinforcements, especially for racing and high-performance vehicles where speed of production and weight reduction are crucial.
2. Aerospace and Aviation: Applied in aircraft structures, interior components, and drone parts that require high strength-to-weight ratios and fast production cycles.
3. Sports Equipment: Utilized in the production of high-end sporting goods such as bicycles, tennis rackets, and hockey sticks, where durability, strength, and lightweight are critical.
4. Wind Energy: Used for creating lightweight and durable wind turbine blades, which benefit from the material's strength and quick curing process.
5. Marine Industry: Employed in the construction of lightweight, high-strength components for boats and yachts, such as hulls and deck structures.
Fast Curing Carbon Fiber Fabric Prepregs Packing:
Our Fast Curing Carbon Fiber Fabric Prepregs are carefully handled during storage and transportation to preserve the quality of our product in its original condition.
Fast Curing Carbon Fiber Fabric Prepregs FAQ:
Q1: What is the curing time for fast-curing carbon fiber fabric prepregs?
A1: The curing time typically ranges from 3 to 10 minutes, depending on the specific resin system and processing conditions used.
Q2: What are the benefits of using fast-curing prepregs compared to traditional prepregs?
A2: Fast-curing prepregs significantly reduce production time while maintaining high strength and performance, allowing for a quicker turnaround in manufacturing processes.
Q3: Can these prepregs be processed using standard composite manufacturing techniques?
A3: Yes, fast-curing carbon fiber fabric prepregs are compatible with various manufacturing techniques, including compression molding, autoclaving, and vacuum bagging.