Fast Curing Glass Fiber Fabric Prepregs Description:
Fast Curing Glass Fiber Fabric Prepregs are high-performance composite materials that utilize a fast-curing epoxy resin system. They cure in as little as 10 minutes at 130°C, significantly reducing production time and costs. With a high glass transition temperature (Tg) of ≥160°C and excellent interlaminar shear strength, these prepregs offer superior thermal and mechanical properties. They are ideal for molding, vacuum bagging, and autoclave processes, and are widely used in industries such as sports equipment, automotive, rail transit, and marine, where lightweight, strong, and durable composite components are essential for efficient manufacturing.
Fast Curing Glass Fiber Fabric Prepregs Specifications:
|
Material
|
Glass Fiber - Epoxy Resin Matrix
|
|
Color/Appearance
|
White Plain/ Twill
|
|
Length
|
100m/roll
|
|
Width
|
1000±5 mm
|
|
Fiber Density
|
200±10 g/m2
|
|
Resin Content
|
Customized
|
|
Prepreg Surface Density
|
Customized
|
|
Curing Conditions
|
130℃/10min
|
Theoretical Mechanical Properties
|
Tensile Strength (MPa)
|
≥400
|
|
Compressive Strength (MPa)
|
≥300
|
|
Flexural Strength (MPa)
|
≥400
|
|
Short Beam Shear (MPa)
|
≥45
|
|
Fiber Volume Fraction
|
55±3%
|
Fast Curing Glass Fiber Fabric Prepregs Applications:
1. Automotive: Used in the production of lightweight body panels, structural components, and reinforcements, reducing vehicle weight while maintaining strength and durability.
2. Sports Equipment: Applied in the manufacturing of high-performance sports gear such as tennis rackets, bicycles, skis, and other equipment where strength and reduced weight are crucial.
3. Rail Transit: Utilized in the production of railcar components, providing lightweight and durable solutions for improved fuel efficiency and performance.
4. Marine: Employed in the construction of boat hulls and other marine structures where corrosion resistance, durability, and reduced weight are critical.
5. Aerospace and Aviation: In the aerospace sector, these prepregs are used to manufacture strong, lightweight components for aircraft structures.
Fast Curing Glass Fiber Fabric Prepregs Packing:
Our Fast Curing Glass Fiber Fabric Prepregs are carefully handled during storage and transportation to preserve the quality of our product in its original condition.
Fast Curing Glass Fiber Fabric Prepregs FAQ:
Q1: What is the curing time and temperature for Fast Curing Glass Fiber Prepregs?
A1: These prepregs cure in just 10 minutes at 130°C, significantly reducing production times compared to traditional prepregs.
Q2: What industries can benefit from using Fast Curing Glass Fiber Prepregs?
A2: These prepregs are ideal for industries such as automotive, sports equipment, rail transit, marine, and aerospace, where lightweight, strong, and durable composite components are needed.
Q3: What is the glass transition temperature (Tg) of the material after curing?
A3: The glass transition temperature (Tg) is ≥160°C, ensuring thermal stability and mechanical performance in high-temperature environments.
Specification
|
Material
|
Glass Fiber - Epoxy Resin Matrix
|
|
Color/Appearance
|
White Plain/ Twill
|
|
Length
|
100m/roll
|
|
Width
|
1000±5 mm
|
|
Fiber Density
|
200±10 g/m2
|
|
Resin Content
|
Customized
|
|
Prepreg Surface Density
|
Customized
|
|
Curing Conditions
|
130℃/10min
|
Theoretical Mechanical Properties
|
Tensile Strength (MPa)
|
≥400
|
|
Compressive Strength (MPa)
|
≥300
|
|
Flexural Strength (MPa)
|
≥400
|
|
Short Beam Shear (MPa)
|
≥45
|
|
Fiber Volume Fraction
|
55±3%
|
.jpg)