| Catalog No. | CM4243 |
|---|---|
| Compositions | Cu, Ni, Si, Cr |
| Appearance | gray powder |
| Particle Size | 20-63 μm |
| Tap Density(g/cm3) | 8.84 |
Copper Alloy CuNi2SiCr Powder is a thermal curable copper alloy. Stanford Advanced Materials (SAM) has rich experience in manufacturing and supplying high-quality Copper Alloy CuNi2SiCr Powder.
Related products: Tungsten Nickel Copper Alloy (W-Ni-Cu Alloy), Molybdenum Copper Alloy
Copper Alloy CuNi2SiCr Powder is a thermal curable copper alloy. It is a favorable combination of electrical and thermal conductivity accompanied by high stiffness, also at elevated temperatures. This copper alloy features a high corrosion resistance and is very well suited for wear and sliding applications.
Chemical Composition (%)
|
Cu |
Ni |
Si |
Cr |
Nb+Ta |
O |
Fe |
Mn |
Pb |
C |
N |
Others Total |
|
Bal. |
2.0-3.0 |
0.5-0.8 |
0.2-0.5 |
/ |
/ |
0.15 |
0.1 |
0.02 |
/ |
/ |
0.1 |
|
Appearance |
gray powder |
|
|
Particle Size |
20-63 μm |
|
|
Tap Density |
8.84 g/cm3 |
|
|
- |
As Built |
Heat Treated |
|
Tensile Strength (MPa) |
314 |
666 |
|
Yield Strength (MPa) |
260 |
580 |
|
Elongation at break (%) |
36 |
18 |
|
Reduction of Area (%) |
79 |
41 |
|
Young’s Modulus (GPa) |
98 |
114 |
Our Copper Alloy CuNi2SiCr Powder is carefully handled during storage and transportation to preserve the quality of our product in its original condition.
CU4273 Tin-Plated Copper Foil
CU4274 Silver-Plated Copper Foil
CM4357 Spherical Brass Alloy (Cu40Zn) Powder
CM4359 Spherical Aluminum Bronze Powder
CU4541 Copper Aluminum Alloy Powder (CuAl)
CU4542 Copper Zirconium Alloy Powder (CuZr)
CU4543 Copper Lanthanum Alloy Powder (CuLa)
CU4544 Silver Copper Alloy Nanopowder (AgCu)
CU4563 Copper Boron Alloy Particles (CuB)
Please fill in your details and one of our material experts will get back to you within 24 hours. For more information, contact us via E-mail at sales@samaterials.com.
** Email address with your company's domain name is preferred. Otherwise, we may not be able to process your inquiry.
Inquiry List