| Catalog No. | MW1398 |
|---|---|
| Purity | 99.9% & 99.99% |
| Appearance | Ingot |
| Product Name | Magnesium (Mg) – Scandium (Sc) Master Alloy/ Mg-Sc |
SAM offers high-quality Magnesium – Scandium (Mg-Sc) Master Alloy with different ratios at competitive prices.
Related Products: Magnesium – Cerium Master Alloy, Magnesium - Gadolinium Master Alloy, Magnesium – Lanthanum Master Alloy
Stanford Advanced Materials provides high purity Magnesium – Scandium (Mg-Sc) Master Alloy with competitive price.
|
Item |
Purity（%） |
Content of Gd |
|
MA-21-1 |
99.9 |
2 ~ 10 ％ |
|
MA-21-2 |
99.99 |
2 ~ 10 ％ |
|
MA-21-C |
99.9 or 99.99 |
Customized |
Main technical indexes & parameters of high strength and high-temperature resistant rare-earth modified Mg alloy
|
Tensile Strength Rm |
Yield Strength Rp0.2 |
Elongation A5 |
Vickers Hardness |
|
280 - 290 Mpa |
140 - 295 Mpa |
6 – 10% |
67 - 63 |
Rare earth (RE) elements have also been successfully alloyed with Mg. The addition of rare-earth (RE) elements can refine grains and weaken anisotropy to improve the ductility of the Mg alloys. In addition, RE elements give rise to a dispersion of thermally stable precipitates with a high melting point (above 620 °C), an improvement over precipitates of the Mg-Zn system which melt at approximately 340°C and thus have poor thermal stability and exhibit tendency for hot tearing.
MW1397 Magnesium – Lanthanum (Mg-La) Master Alloy
MW1399 Magnesium – Yttrium (Mg-Y) Master Alloy
MW1400 Magnesium – Neodymium (Mg-Nd) Master Alloy
MW1401 Magnesium –Zirconium (Mg-Zr) Master Alloy
MW1654 Magnesium Barium Master Alloy
MW1655 Magnesium Calcium Master Alloy
MW1656 Magnesium Dysprosium Master Alloy
MW1915 Magnesium Nickel (Mg-Ni) Master Alloy
Please fill in your details and one of our material experts will get back to you within 24 hours. For more information, contact us via E-mail at sales@samaterials.com.
** Email address with your company's domain name is preferred. Otherwise, we may not be able to process your inquiry.