Catalog No. | CA3518 |
---|---|
Chemical Formula | TaC, NbC |
Form | dark grey powder |
Purity | 99% |
Tantalum Carbide- Niobium Carbide (90:10) Solid Solution Powder is a kind of dark grey powder with a chemical formula of TaC, NbC. Stanford Advanced Materials (SAM) offers high-quality Tantalum Carbide- Niobium Carbide (90:10) Solid Solution Powder with competitive pricing.
Related products: Tantalum Carbide Powder, Niobium Carbide Powder, Titanium Carbide Powder
Tantalum Carbide- Niobium Carbide (90:10) Solid Solution Powder is a kind of dark grey powder. It is a solid solution referring to an alloy phase in which solute atoms dissolve into the solvent crystal lattice while still maintaining the solvent type.
Grade |
90: 10 |
||
Chemical composition |
Ta |
84.4±1.5 |
|
Nb |
8.85±1.0 |
||
T.C |
6.75±0.3 |
||
F.C |
≤0.15 |
||
Impurities content |
Co |
0.1 |
|
Mo |
0.1 |
||
Si |
0.02 |
||
Fe |
0.15 |
||
Ni |
0.04 |
||
K |
0.008 |
||
Na |
0.008 |
||
Mn |
0.05 |
||
Sn |
0.01 |
||
Ca |
0.01 |
||
Al |
0.015 |
||
N |
0.25 |
||
O |
Grade 1 |
0.35 |
|
Grade 2 |
0.25 |
||
Grade 3 |
0.2 |
||
Ti |
0.2 |
||
W |
0.2 |
||
Cr |
0.1 |
For cemented carbide.
Our Tantalum Carbide- Niobium Carbide (90:10) Solid Solution Powder is carefully handled during storage and transportation to preserve the quality of our product in its original condition.
CA3519 Tantalum Carbide- Niobium Carbide (80:20) Solid Solution Powder
CA3521 Tantalum Carbide- Niobium Carbide (60:40) Solid Solution Powder
CA3522 Tantalum Carbide- Niobium Carbide (50:50) Solid Solution Powder
CA3523 Tungsten-Titanium-Tantalum Carbide Solid Solution Powder (WC/TiC/TaC)
CA3524 Tungsten-Titanium-Tantalum (Niobium) Carbide Solid Solution Powder (WC/TiC/TaC(NbC))
CA3525 Duplex Carbide (WC/TiC)
TS3527 Spray Powder (WC-10Co-4Cr)
CB3827 Monolayer Molybdenum Carbide (Mo2C)
Please fill in your details and one of our material experts will get back to you within 24 hours. For more information, contact us via E-mail at sales@samaterials.com.
** Email address with your company's domain name is preferred. Otherwise, we may not be able to process your inquiry.