Catalog No. | FE2603 |
---|---|
Size | Customized |
Shape | Flat Bar |
Other trade name | UNS T11307, AISI M7 Steel |
M7 High-Speed Tool Steel Flat Bar has high wear resistance. Stanford Advanced Materials (SAM) is a trustworthy supplier of M7 High-Speed Tool Steel Flat Bar and provides customers with various shapes of high-speed tool steel according to their requirements.
Other shapes of AISI M7 Steel: Plate, round wire, round bar, flat wire
Related products: Tungsten Carbide Die, TZM alloy
M7 High-Speed Tool Steel Flat Bars contain chromium, tungsten, and vanadium for strengthening. They are mainly used for cutting tools in all machining operations thanks to their high hardness, high wear resistance, and high heat resistance. Stanford Advanced Materials (SAM) is a trustworthy supplier of M7 High-Speed Tool Steel Flat Bar and can provide customers with various shapes of high-speed tool steel.
Element | C | Mn | Si | Cr | Ni | Mo | V | Cu | P | S | Fe |
Content | 0.84-1.05% | 0.10-0.40% | 0.20-0.45% | 3.75-4.50 % | 0.30% | 7.75-8.50% | 1.80-2.20% | 0.25% | 0.03% | 0.03% | Remainder |
Density | Melting point | Forging ratio | Annealing temperature | Hardening temperature | Commonly used drawing temperature | After tempering hardness HRC |
8.9 kg/m3 | 1427 °C | 5:1 minimum | 750~790 °C | 1204 °C | 552 °C | 65HRC Min |
- Cutting tools in all machining operations
- Fine hand tools where their relatively good toughness at high hardness
FE4417 Pre-alloyed Powder FeCu10
FE4418 Pre-alloyed Powder FeCu18
FE4419 Pre-alloyed Powder FeCu30
FE4420 Pre-alloyed Powder FeCu40
FE4421 Pre-alloyed Powder Fe-Cu-Co-Ni
FE4422 Reinforced Alloy Powder Fe-Ni-Co-P-Re
FE4415 Pre-alloyed Powder FeCu20
FE4546 FeNi Powder for Diamond Tool
FE4547 FeMn Powder for Diamond Tool
Please fill in your details and one of our material experts will get back to you within 24 hours. For more information, contact us via E-mail at sales@samaterials.com.
** Email address with your company's domain name is preferred. Otherwise, we may not be able to process your inquiry.